LB-K Economical Cross-Linked Film /

LB-K Economical Cross-Linked Film

LB-K is a cross-linked polyolefin shrink film with perfect combination of performance and high yield. It has comparable performance as LB-C, but with cost savings through higher yield. The higher yielding with low gauges provide lower film cost per package and the high efficiency during packaging process due to less roll changes. This film is suitable for nearly all sealing systems because of its high strength and high seal performance.

Thickness10um、13um、17um、22um

LB-K.pdf

Technical Index

TEST ITEM		UNIT	ASTM TEST	TYPICAL VALUES

GAUGE				10um	13um	17um	22um
TENSILE STRENGTH
Tensile Strength (MD)		N/mm2	D882	130	130	130	125
Tensile Strength (TD)				125	125	125	120
Elongation
Elongation(MD)		%	D882	110	115	118	120
Elongation (TD)				105	110	108	115
TEAR
MD at 400gm		g	D1922	9	14.0	16.5	22.5
TD at 400gm				9.5	13.0	18.5	23.5
SEAL STRENGTH
MD\Hot Wire Seal		N/mm	F88	0.96	1.20	1.25	1.50
TD\Hot Wire Seal				1.06	1.35	1.45	1.65
COF (Film To Film)
Static			D1894	0.24	0.21	0.18	0.19
Dynamic				0.24	0.21	0.18	0.19
OPTICS
Haze			D1003	2.2	2.4	2.6	2.9
Clarity			D1746	98.5	98.5	98.0	98.0
Gloss @ 45Deg			D2457	89.0	88.5	88.0	86.5
BARRIER
Oxygen Transmission Rate		cc/㎡/day	D3985	12100	9700	7400	6800
Water Vapor Transmission Rate		gm/㎡/day	F1249	40.5	32.5	25.3	19.5
SHRINKAGE PROPERTIES				MD		TD
Free Shrinkage	100℃	%	D2732	18		28
	110℃			37		45
	120℃			70		72
	130℃			81		79
				MD		TD
Shrink Tension	100℃	Mpa	D2838	2.20		2.65
	110℃			2.66		3.80
	120℃			2.85		4.00
	130℃			2.80		3.90

Note: The above information is based on our internal evaluation data and is for reference only.